The ferrite  content,in  percentage  by  surface/volume  fraction,shall  be  as  stated  below  for  all  duplex  grades:

铁素体含量，以表面/体积分数的百分比表示，应如下所述，适用于所有双相等级：

—35%to   60%in   base   material;

— 基材中为35%至60%;

—35%to  65%in  solution   heat   treated  weld   metals;

—在固溶热处理的焊接金属中为35%至65%;

—30%to  70%for  welds   in  the  as  welded  condition.

一对于处于焊接状态的焊缝，30%至70%。